低品位高钛渣中钛组分制备金红石.docx

低品位高钛渣中钛组分制备金红石低品位高钛渣中钛组分制备金红石摘要：介绍了以70％～75％TiO2的低品位高钛渣为原料制备人造金红石的分离工艺.低品位高钛渣中MgO,FeO,CaO,Al2O3和SiO2进入杂质相,钛组分进入金红石相,金红石相中TiO2品位达到90％～95％,可满足流态化氯化对杂质的要求.1050℃的低温预氧化与1510℃的高温热处理促使渣中分散于各矿物相的.钛组分选择性转移并富集于金红石相,金红石相析出与长大,用稀硫酸和稀盐酸实现金红石相的分离.实验结果表明,金红石矿物相平均晶粒度可以达到25μrn,通过稀酸选择性浸出改性渣,可以获得95％TiO2品位的人造金红石.Abstract：Anewtechniquewasdevelopedfortheconversionofhightitaniaslag,containing70％-75％TiO2andwithMgO,FeO,CaO,Al2O3andSiO2asmainimpurities,intoasyntheticrutile,90％-95％TiO2,whichsatisfiestherequirementsforfluidizingchlorinationprocesswithrespecttoimpuritycontents.Afterapre-oxidationataround1042℃andaheat-treatmentabove1510℃,theTicomponentsinhightitaniaslagcanbeenrichedintotherutilephasewhichcanprecipitateandgrow,andcanbeseparatedwithdilutehydrochloricandsulfuricacid,respectively.Theresultsshowthattheaveragecrystalsizeofrutilephaseisover25μm,andthesyntheticrutilecontainingmorethan95％TiO2canbeproducedbyselectiveleaching.作者：张力[1]  李光强[2]  张武[1]Author：ZHANGLi[1]  LIGuang-qiang[2]  ZHANGWu[1]作者单位：东北大学材料与冶金学院,沈阳,110004武汉科技大学材料与冶金学院,武汉,430081期刊：中国有色金属学报（英文版） ISTICEISCIJournal：TransactionsofNonferrousMetalsSocietyofChina年，卷(期)：2011, 21(10)分类号：Q51关键词：高钛渣  氧化  浸出  金红石  Keywords：hightitaniaslag  oxidation  leaching  rutile  机标分类号：TQ1TU5机标关键词：低品位    高钛渣    原料制备    金红石相    high    TiO2    人造金红石    averagecrystalsize    sulfuricacid    newtechnique    矿物相    选择性转移    选择性浸出    平均晶粒度    高温热处理    低温预氧化    Al2O3    质的要求    实验结果    分离工艺基金项目：theOpenResearchFundofKeyLaboratoryforFerrousMetallurgyandRes