固溶处理对镁合金组织和耐腐蚀性能的影响毕业论文.doc

长春工业大学本科毕业论文PAGE\*MERGEFORMAT42摘要论述了Mg-Al-Zn系合金经过固溶处理后组织和耐腐蚀性能的变化。通过观察经固溶处理后的组织及塔菲尔曲线，对Mg-Al-Zn系合金固溶处理后的组织和电化学腐蚀行为进行了研究。结果表明，经过固溶处理后的镁合金显微组织晶粒长大明显，β-（Mg17Al12）相部分溶解在基体组织中，在温度达到560度以上时，组织发生过烧现象。与未经处理镁合金的耐腐蚀性能相比，经过固溶处理后的镁合金耐腐蚀性能无明显增加。关键词：镁合金；固溶处理；显微组织；耐腐蚀性能Title:SolutionTreatmentonMg-Al-ZnalloysorganizationsandtheimpactofcorrosionresistanceAbstractDiscussestheMg-Al-Znalloyaftersolutiontreatmentandcorrosionresistanceaftertheorganizationchanges.ByobservingtheorganizationaftersolutiontreatmentandtheTafelcurvesofMg-Al-Znalloyaftersolutiontreatmentandelectrochemicalcorrosionbehaviorwasstudied.Theresultsshowedthat,afterthemagnesiumalloyaftersolutiontreatmentmicrostructuregraingrowthsignificantly,β-(Mg17Al12)phasepartiallydissolvedinthematrixorganization,inthetemperaturereaches560degrees,thetissueover-burningphenomenon.Withuntreatedcorrosionresistanceofmagnesiumalloyscomparedtothatafterthemagnesiumalloyaftersolutiontreatmentdidnotincreasethecorrosionresistance.Keywords：Magnesiumalloy；Microstructure；Corrosionresistance学位论文原创性声明本人郑重声明：所呈交的论文是本人在导师的指导下独立进行研究所取得的研究成果。除了文中特别加以标注引用的内容外，本论文不包含任何其他个人或集体已经发表或撰写的成果作品。对本文的研究做出重要贡献的个人和集体，均已在文中以明确方式标明。本人完全意识到本声明的法律后果由本人承担。作者签名：日期：年月日学位论文版权使用授权书本学位论文作者完全了解学校有关保留、使用学位论文的规定，同意学校保留并向国家有关部门或机构送交论文的复印件和电子版，允许论文被查阅和借阅。本人授权大学可以将本学位论文的全部或部分内容编入有关数据库进行检索，可以采用影印、缩印或扫描等复制手段保存和汇编本学位论文。涉密论文按学校规定处理。作者签名：日期：年月日导师签名：日期：年月日目录TOC\o"1-4"\h\uHYPERLINK\l"_Toc295479717"目录PAGEREF_Toc295479717\h3HYPERLINK\l"_Toc295479718"第一章绪论PAGEREF_Toc295479718\h4HYPERLINK\l"_Toc295479719"1.1选题的目的与意义PAGEREF_Toc295479719\h4HYPERLINK\l"_Toc295479720"1.2镁合金PAGEREF_Toc295479720\h5HYPERLINK\l"_Toc295479721"1.2.1镁合金的发展PAGEREF_Toc295479721\h5HYPERLINK\l"_Toc295479722"1.2.2镁合金的性能及应用PAGEREF_Toc295479722\h6HYPERLINK\l"_Toc295479723"1.2.2.1镁合金在汽车上的应用：PAGEREF_Toc295479723\h6HYPERLINK\l"_Toc295479724"1.2.2.2镁合金在3C产品上的应用：PAGEREF_Toc295479724\h7HYPERLINK\l"_Toc295479725"1.2.3镁合金的种类及发展趋势PAGEREF_Toc295479725\h7HYPERLINK\l"_Toc2