2022a2S破络与混凝沉淀组合处理电镀废水的研究.docx

Na2S破络与混凝沉淀组合处理电镀废水的研究摘要：电镀废水不仅能够污染环境，并且对人体造成伤害。本文通过Na2S破络与混凝沉淀组合处理电镀废水中Cu2+与COD，分析了Na2S投加量、初始pH值与反应时间等因素对电镀废水处理效果的影响。结果表明，最佳处理条件为：Na2S投加量100mg/L，初始pH值7.5，反应时间选择15min，PAC混凝pH为7.5，PAC投加量为8.0mg/L，混凝时间为6min，PAMmg/L，沉降时间为50min，出水中Cu2+浓度为0.43mg/L，COD浓度为41.26mg/L，能够达到电镀废水排放标准。关键字：Na2S；电镀废水；Cu2+；COD；混凝沉淀StudyontheTreatmentofElectroplatingWastewaterbytheCombinationofNa2SNetworkandCoagulationSedimentationAbstract:Electroplatingwastewatercannotonlypollutetheenvironment,butalsocauseharmtothehumanbody.Inthispaper,Cu2+andCODinelectroplatingwastewaterweretreatedbycombinationofNa2Snetworkandcoagulationandsedimentation.Theeffectsofdosageofsodiumsulfide,initialpHvalueandreactiontimeonelectroplatingwastewatertreatmentwereanalyzed.TheresultsshowedthattheoptimaltreatmentconditionswereNa2Sdosage100mg/L,initialpH7.5,reactiontime15min,PACcoagulationpH7.5,PACdosage8.0mg/L,coagulationtimeThedosageofPAMwas8.0mg/L,thesettlingtimewas50min,theconcentrationofCu2+intheeffluentwas0.46mg/LandtheCODconcentrationwas60.96mg/Lat6min,whichcouldmeettheelectroplatingwastewaterdischargestandards.Keywords:Na2S;electroplatingwastewater;Cu2+;COD;coagulationandsedimentation;0引言电镀废水作为工业最难处理的废水之一[1]，其主要成分包括重金属废水与有机废水，重金属废水大部分为金属络合形态，水质复杂难以处理。化学沉淀法是一种比较成熟的废水处理方法，利用Na2S处理废水不仅能够破坏重金属的络合形态，而且可以形成硫化物沉淀，达到去除废水中污染物的目的。混凝沉淀法是一种废水中悬浮态污染物的处理方法[2]，能够做到对废水深度处理。本文首先通过Na2S对电镀废水进行破络处理，然后利用混凝剂PAC与助凝剂PAM进行沉降处理，分析了Na2S投加量、初始pH值与反应时间等因素对废水处理效果的影响，得到了废水处理的最佳工艺条件。1实验材料及方法实验仪器及试剂实验所用化学试剂包括：氢氧化钠（AR），Na2S（AR）、硫酸亚铁（AR）、硫酸银（AR）、重铬酸钾（AR）、硫酸亚铁铵（AR）、硫酸（AR），天津市恒山化工科技。聚合氯化铝（PAC）与聚丙烯酰胺（PAM），工业级，巩义市先科净水材料厂。实验所用仪器包括：PHS-3C型pH计，；FA2204型电子天平，；SHZ-A型水浴恒温振荡器，；WFX−120型原子吸收分光光度计，日本岛津仪器厂。实验废水：合肥市某电子公司的实际废水，Cu2+的质量浓度为84.32mg/L，COD的质量浓度为2242.39mg/L。1.2实验工艺流程图1Na2S混凝沉淀法处理电镀废水的工艺流程1.3实验方法Na2S破络：500mL烧杯中加入250mL废水，通过10mol/LNaOH溶液调节不同的pH值，加入不同质量的Na2S，200rpm的条件下反应一定的时间，沉淀90m