聚羧酸减水剂的合成工艺及性能研究.doc

一种新型聚醚类聚羧酸减水剂的合成工艺及性能研究摘要：采用奥克公司的新型聚醚OXAB-608和丙烯酸为聚合单体，通过水溶液自由基聚合合成了减水剂，研究了合成工艺对减水剂性能的影响规律。结果表明：当聚醚与丙烯酸摩尔比为4.5，引发剂用量为聚合单体总质量的0.5%，链转移剂用量为聚合单体用量的0.17%，反应温度为60℃时，合成的聚羧酸减水剂在掺量为水泥质量的2.0%时，减水剂效果最好。关键词：聚羧酸减水剂，丙烯酸，聚醚，自由基聚合SynthesisandPropertiesofnewpolyetherpolycarboxylatesuperplasticizerSungui-e，Fanlei，Fuyang，Zhouli-ming，Liuzhao-bin，Zhujian-min(LiaoningOxiranchem.GROUPCO.,LTD,LiaoningLiaoyang111003)Abstract:oxiranchemcorporation'snewpolyetherwithOXAB-608andacrylicacidasmonomerwassynthesizedbyaqueoussolutionradicalpolymerizationwater-reducingagenttostudythepropertiesofthesynthesisprocessonwater-reducingagentwereinvestigated.Theresultsshowedthat:Whentheetherwithacrylicacidmolarratioof4.5,triggeringagentisthetotalmassofmonomer0.5%,chaintransferagentis0.17%ofmonomeramount,thereactiontemperatureis60℃,thesynthesizedpoly-carboxylicacidwaterreducerforcementqualityintheash2.0%,thewaterreducerbestresults.Keywords:polycarboxylatewaterreducer,acrylicacid,polyether,freeradicalpolymerization1、前言高效减水剂又称超塑化剂，它的两种基本作用是使混凝土的水胶比降到最低和流动性达到最大。进入21世纪，高效减水剂应是性能更好、更能满足实际需要的高性能减水剂，除具有高效减水、改善混凝土孔结构和密实程度等作用外，还能控制混凝土的塌落度损失，更好地解决混凝土的引气、缓凝、泌水等问题1李崇智,李永德,冯乃谦.聚羧酸减水剂的合成工艺研究J.混凝土,2001(5)3-6.2李崇智,冯乃谦,李永德.一种新型聚梭酸系高性能减水剂的作用机理及其应用J.化学建材，2002，30-33．1。（甲氧基）聚乙二醇单（甲基）丙烯酸酯类减水剂分散性和保塌性较好，并且水泥适应性强，被广泛应用。但是其合成工艺需要酯化和聚合两部分，生产周期长，且操作麻烦，成本高，正逐渐被醚类聚羧酸减水剂所替代。现在市场上广泛应用的醚类减水剂性能最好的产品是，使用OXAB-501聚醚结构类型合成的减水剂产品，但是合成的减水剂产品的价格也较高，本文采用辽宁奥克化学股份有限公司的新型OXAB-608聚醚为原料，合成减水剂的应用性能已达到或超过使用OXAB-501聚醚合成的减水剂产品的性能，且减水剂成本比使用OXAB-501聚醚合成的减水剂成本低，性价比更高。2、实验2.1原料及仪器本实验原料：OXAB-608聚醚（辽宁奥克化学股份公司生产），工业级；丙烯酸，工业级；引发剂A、B和链转移剂C；氢氧化钠，工业级；去离子水；基准水泥；标准砂。本实验设备：四口烧瓶，温度计，搅拌器，蠕动泵，砂浆机。2.2聚合试验方法先将一定量的OXAB-608聚醚与蒸馏水加入到烧瓶中，搅拌升温到指定温度，首先加入A的水溶液，然后用蠕动泵开始分别滴加AA水溶液与B和C的水溶液，AA水溶液滴加3～3.5h，B和C的水溶液滴加3.5～4h，保温老化1h，用30%的氢氧化钠溶液中和至ph=6-7，即得减水剂。2.3净浆评价实验水泥砂浆流动度测定方法，基准水泥P.O.42.5，水灰比0.416，减水剂掺量0.2%（固体质量与水泥质量百分比，以下同）。具体配比如