【精编】a2S破络与混凝沉淀组合处理电镀废水的研究.docx

Na2S破络与混凝沉淀组合处理电镀废水的研究摘要：电镀废水不仅能够污染环境并且对人体造成伤害。本文通过Na2S破络与混凝沉淀组合处理电镀废水中Cu2+与COD分析了Na2S投加量、初始pH值与反应时间等因素对电镀废水处理效果的影响。结果表明最佳处理条件为：Na2S投加量100mg/L初始pH值7.5反应时间选择15minPAC混凝pH为7.5PAC投加量为8.0mg/L混凝时间为6minPAMmg/L沉降时间为50min出水中Cu2+浓度为0.43mg/LCOD浓度为41.26mg/L能够达到电镀废水排放标准。关键字：Na2S；电镀废水；Cu2+；COD；混凝沉淀StudyontheTreatmentofElectroplatingWastewaterbytheCombinationofNa2SNetworkandCoagulationSedimentationAbstract:Electroplatingwastewatercannotonlypollutetheenvironmentbutalsocauseharmtothehumanbody.InthispaperCu2+andCODinelectroplatingwastewaterweretreatedbycombinationofNa2Snetworkandcoagulationandsedimentation.TheeffectsofdosageofsodiumsulfideinitialpHvalueandreactiontimeonelectroplatingwastewatertreatmentwereanalyzed.TheresultsshowedthattheoptimaltreatmentconditionswereNa2Sdosage100mg/LinitialpH7.5reactiontime15minPACcoagulationpH7.5PACdosage8.0mg/LcoagulationtimeThedosageofPAMwas8.0mg/Lthesettlingtimewas50mintheconcentrationofCu2+intheeffluentwas0.46mg/LandtheCODconcentrationwas60.96mg/Lat6minwhichcouldmeettheelectroplatingwastewaterdischargestandards.Keywords:Na2S;electroplatingwastewater;Cu2+;COD;coagulationandsedimentation;0引言电镀废水作为工业最难处理的废水之一[1]其主要成分包括重金属废水与有机废水重金属废水大部分为金属络合形态水质复杂难以处理。化学沉淀法是一种比较成熟的废水处理方法利用Na2S处理废水不仅能够破坏重金属的络合形态而且可以形成硫化物沉淀达到去除废水中污染物的目的。混凝沉淀法是一种废水中悬浮态污染物的处理方法[2]能够做到对废水深度处理。本文首先通过Na2S对电镀废水进行破络处理然后利用混凝剂PAC与助凝剂PAM进行沉降处理分析了Na2S投加量、初始pH值与反应时间等因素对废水处理效果的影响得到了废水处理的最佳工艺条件。1实验材料及方法实验仪器及试剂实验所用化学试剂包括：氢氧化钠（AR）Na2S（AR）、硫酸亚铁（AR）、硫酸银（AR）、重铬酸钾（AR）、硫酸亚铁铵（AR）、硫酸（AR）天津市恒山化工科技。聚合氯化铝（PAC）与聚丙烯酰胺（PAM）工业级巩义市先科净水材料厂。实验所用仪器包括：PHS-3C型pH计；FA2204型电子天平；SHZ-A型水浴恒温振荡器；WFX−120型原子吸收分光光度计日本岛津仪器厂。实验废水：合肥市某电子公司的实际废水Cu2+的质量浓度为84.32mg/LCOD的质量浓度为2242.39mg/L。1.2实验工艺流程图1Na2S混凝沉淀法处理电镀废水的工艺流程1.3实验方法Na2S破络：500mL烧杯中加入250mL废水通过10mol/LNaOH溶液调节不同的pH值加入不同质量的Na2S200rpm的条件下反应一定的时间沉淀90min过滤测定滤液中Cu2+与COD的含量。混凝沉淀：Na2S沉淀之后调节不同的pH值加入不同质量的混凝剂PAC200rpm反应一定的时间