稀土对含铌钢组织和性能的影响.docx

编号：时间：2021年x月x日书山有路勤为径学海无涯苦作舟页码：稀土对含铌钢组织和性能的影响朱兴元陈邦文姜凤琴曾静朱天佑林勤摘要：研究了稀土对含铌钢组织和性能的影响研究结果表明稀土元素的加入使钢的纵横向强度先下降而后上升钢的延伸率和冲击功则先上升而后下降其对改善钢的强度和-20℃以下冲击功的各向异性不明显而且对细化晶粒度和夹杂物级别影响不显著但稀土元素的加入使铌的析出量略有增加。关键词：稀土含铌钢性能ROLEOFRAREEARTHINNb-BEARINGSTEELZhuXingyun（WuhanIron&SteelCorp.）ChengBangwen（WuhanIron&SteelCorp.）JiangFengqin（WuhanIron&SteelCorp.）ZengJing（WuhanIron&SteelCorp.）ZhuTianyou（UniversityofScience&TechnologyBeijing）Linqin（UniversityofScience&TechnologyBeijing）Abstract：EffectsofrareearthonthemicrostructureandpropertiesofNb-bearingsteelhavebeeninvestigated.Resultsprovethatadditionofrareearthelementsintothesteelcausesthetransversalandlongitudinalstrengthofthestrengthdeclineinitiallyandriseafterwardandtheelongationandimpactenergyofthesteelchangeinthereversaldirection.Astheresultsadditionofrareearthinthesteelcouldhardlyimprovethestrengthanistropismandimpacttoughnessbelow-20℃anditseffectsonthegrainrefiningandinclusionsizeimprovementarealsonegligiblehoweveritcouldprobablyofferaslightincreaseinNbprecipitation.Keywords：rareearthNbbearingsteelproperty1前言近几十年来随着微合金化元素Nb、V、Ti在钢中的广泛应用使得微合金化钢得到了迅速发展而微合金化元素Nb、V、Ti主要是利用其碳氮化物应变诱导析出与高温形变再结晶的交互作用产生晶粒细化以及沉淀强化的效果来提高材料的强度和韧性但钢中其它元素的存在会对碳氮化物的沉淀析出反应产生影响因此在含铌钢中稀土元素的加入同样会影响到其强化效果研究表明［1］稀土在奥氏体相温度范围可以阻止铌沉淀相的析出过程并且有迹象显示:在奥氏体相区及铁素体相区稀土对含铌沉淀相析出的作用规律可能不同因此本研究主要开展稀土对含铌钢作用的研究探寻稀土在含铌钢中的作用规律探讨不同稀土含量对含铌钢的组织、性能以及沉淀相析出规律的影响。2试验条件和试验方案试验钢在50kg真空感应炉中冶炼稀土为含铈量大于99%的纯铈金属稀土在冶炼终点和出钢前加入试验钢的化学成分见表1。表1稀土微合金钢化学成分(w)%编号SiMnPNbCSRE10.211.200.0160.0390.0670.0045020.191.200.0150.0380.0680.00390.032530.171.190.0150.0410.0520.00300.049540.181.180.0160.0340.0530.00270.092050.181.160.0160.0410.0500.00440.1540试验钢先采用铝线进行脱氧处理后使用氩气保护注锭钢锭为50kg的圆锭钢锭在1200℃加热保温2h在小轧机上进行两阶段控轧开轧温度1150℃再结区轧制温度为1000～1150℃非再结晶区轧制温度为800～950℃之间进行具体轧制工艺参数见表2所示。表2轧制工艺参数项目初轧精轧道次1234567温度/℃＞1000＞1000＞10