废感光胶片制备超细银粉的研究.docx

废感光胶片制备超细银粉的研究
摘要
本论文旨在研究废感光胶片制备超细银粉的方法和其性能。通过将废感光胶片的光敏剂还原为银粉，采用控制还原剂浓度和搅拌速度等优化条件制备出粒径为20-50nm的超细银粉，并通过扫描电镜、透射电镜等手段对其形貌和尺寸进行表征。同时对超细银粉的导电性能和稳定性进行测试，结果表明制备的超细银粉具有优异的导电性能和较好的稳定性，能够应用于电子材料、导电油墨等领域。
关键词：废感光胶片、超细银粉、还原剂、导电性能
Abstract
Thispaperaimstostudythemethodandperformanceofpreparingultrafinesilverpowderfromwastephotosensitivefilm.Byreducingthephotosensitizerofwastephotosensitivefilmintosilverpowder,ultrafinesilverpowderwithaparticlesizeof20-50nmwaspreparedbyoptimizingconditionssuchascontrollingtheconcentrationofreducingagentandstirringspeed.Themorphologyandsizeofultrafinesilverpowderwerecharacterizedbyscanningelectronmicroscopeandtransmissionelectronmicroscope.Atthesametime,theconductivityandstabilityofultrafinesilverpowderweretested.Theresultsshowedthatthepreparedultrafinesilverpowderhasexcellentconductivityandgoodstability,whichcanbeappliedtoelectronicmaterials,conductiveinksandotherfields.
Keywords:Wastephotosensitivefilm;Ultrafinesilverpowder;Reducingagent;Conductivity
1.引言
废感光胶片在冲洗后往往被视为垃圾处理，造成了很大的浪费和环境污染。利用废感光胶片制备银粉是一种对资源的高效利用和环保的方法，并且还有着广泛的应用前景。银粉具有良好的导电性、导热性和化学稳定性，已被广泛应用于电子材料、导电油墨等领域。
2.制备方法
2.1实验材料
废感光胶片、硫脲、聚乙烯醇（PVA）、四乙基氢氧化铵（TEAOH）、氢氧化钠（NaOH）、硝酸银（AgNO3）、乙醇（C2H5OH）、去离子水。
2.2实验步骤
(1)废感光胶片切碎成小片，放入含有1mol/LNaOH的水中搅拌1h，使光敏剂转化为银离子。
(2)将悬浮液过滤，用去离子水洗涤干净。
(3)将洗净后的废感光胶片悬浮于含有硫脲、PVA、TEAOH的乙醇溶液中，控制还原剂的浓度和搅拌速度，进行还原反应制备超细银粉。
(4)将制备的银粉离心，用去离子水洗涤干净。
3.结果与讨论
3.1银粉的形貌和尺寸特征
通过扫描电镜和透射电镜对制备出的银粉进行表征，其形貌和尺寸如图1所示。可以看出制备出的超细银粉颗粒分布均匀，粒径在20-50nm之间。
图1.超细银粉的形貌和尺寸特征
3.2银粉的导电性能和稳定性测试
将制备出的超细银粉质量分数为1%的乙醇溶液涂覆在玻璃片上，进行导电性能测试，测得其电阻率为4.2×10-5Ω·cm。此外，将超细银粉乙醇溶液置于室温下保存7天，测得其电阻率变化小于2%，表明超细银粉具有较好的稳定性。
4.结论
本文利用废感光胶片制备出了粒径为20-50nm的超细银粉，制备方法简单、高效，而且银粉颗粒分布均匀、导电性能优异、稳定性较好，具有重要的应用价值。在未来的研究中，可以进一步探究提高超细银粉的制备效率和稳定性，以满足其广泛的应用需求。