细鳞片膨胀石墨&聚苯胺导电复合材料的制备研究

摘要

以十二烷基苯磺酸钠为乳化剂，过硫酸铵为聚合引发剂，盐酸和细鳞片膨胀
石墨为掺杂剂，利用乳液聚合法制备了细鳞片膨胀石墨&聚苯胺导电复合材料。系统研究了膨胀石墨的掺杂量、盐酸用量、乳化剂及引发剂对电导率的影响。最佳实验条件为：石墨掺杂6%，盐酸6mL，乳化剂5g，引发剂3.25g。此条件下的电导率为0.75S/cm。
通过超声波搅拌预插层法制备了纳米膨胀石墨&聚苯胺复合材料。XRD分析
表明，苯胺已有效插入石墨层间并且聚合。SEM分析表明复合材料粒度较为均匀，形成了剥离性的复合材料。

关键词聚苯胺，膨胀石墨，导电性，乳液聚合，超声波，插层

ABSTRACT
UsingSDBSasemulsifier,ammoniumsulfateaspolymerizationinitiator,
hydrochloricacidandfineflakeexpansiongraphiteasdopingagents,fineflakeexpandedgraphite&polyanlinecompositematerialwaspreparedbyemulsion.Theeffectsofvariousconditionsofpreprationoffineflakeexpandedgraphite&polyanlinecompositematerialonitsconductivitywasinvestgatedsystematically.Theoptimumconditionswere6%fineflakeexpandedgraphite,6mLhydrochloricacid,5gemulsifier,3.25ginitiator.Undertheseconditions,theconductivityis0.75S/cm.
Thepolyanilineexpandedgraphitecompositematerialwaspreparedbyultrasound
Stiringpre-intercalationandwascharacterizedusingXRDandSEMtechniques.Theresultsprovedthattheanilinehaseffectivelyinsertedbetweenthelayersofgraphiteandpolymerizationandthatcompositematerialshasuniformsizeandfragmentation.

KeywordsPolyaniline,Expandedgraphite,Emulsionpolymerization，Intercalation
目录

TOC\o"1-3"\u摘要 PAGEREF_Toc200979263\hI
ABSTRACT PAGEREF_Toc200979264\hII
1绪论 PAGEREF_Toc200979265\h1
1.1课题背景 PAGEREF_Toc200979266\h1
1.2膨胀石墨 PAGEREF_Toc200979267\h1
1.2.1石墨的基本性质 PAGEREF_Toc200979268\h1
1.2.2膨胀石墨的应用 PAGEREF_Toc200979269\h1
1.3聚苯胺 PAGEREF_Toc200979270\h3
1.3.1聚苯胺的结构 PAGEREF_Toc200979271\h3
1.3.2聚苯胺的性质 PAGEREF_Toc200979272\h3
1.4聚苯胺的复合改性 PAGEREF_Toc200979273\h4
1.4.1聚苯胺/聚合物复合材料 PAGEREF_Toc200979274\h4
1.4.2聚苯胺/无机物复合材料 PAGEREF_Toc200979275\h5
1.5膨胀石墨/聚苯胺复合材料的研究现状 PAGEREF_Toc200979276\h6
1.6本课题的研究内容 PAGEREF_Toc200979277\h7
2复合材料制备实验条件的确定 PAGEREF_Toc200979278\h8
2.1实验药品及仪器 PAGEREF_Toc200979279\h8
2.1.1实验药品 PAGEREF_Toc200979280\h8
2.1.2实验仪器 PAGEREF_Toc200979281\h8
2.2实验方案 PAGEREF_Toc200979282\h8
2.3细鳞片膨胀石墨的制备 PAGEREF_Toc200979283\h